As a non-shrink filler and repair compound, which can be overcoated with either an epoxy or polyester/vinyl ester top coat. It may also be used as a standalone grouting or filling compound.

Consult the Health & Safety data sheet prior to carrying out any work with this product. Surface preparation For the best result, the surface should be blast cleaned to ISO8501-1 Sa 2½ with a 75micron profile. If grit blasting is not possible the surface should be degreased, loose material removed and the surface roughened to obtain a suitable key.

Short hair stiff brush, trowel, float or mastic type gun. Mixing Remove the lids from both the base and activator. Add between 1% and 2% of adhesion promoter to the base and mix in thoroughly. Add all of the activator to the base and mix thoroughly, ensuring no unmixed material remains. Remove all the mixed material from the base tin and re-mix on a clean
flat surface or in a clean shallow receptacle. This product has a relatively short pot life, mix only as much material as you can apply within this period.

This material is intended for use as a filler or grouting material and can be built up to the required film thickness. It should, where possible be applied over a primer layer or correctly
prepared substrate. Application of films greater than 6mm in one coat should be avoided, to prevent excessive exotherms during cure. Incorporation of the adhesion promoter will
substantially improve the bond in all cases, both intercoat and to the substrate.

2 Parts base to 1 part activator by weight.

40 Minutes at 20°C, shorter at higher temperatures and longer at lower temperatures. DO NOT APPLY AT TEMPERATURES BELOW 5°C OR WHEN SUBSTRATE TEMPERATURE IS LESS THAN 3°C ABOVE DEW POINT. Thinners DO NOT THIN. Addition of solvent will detract from the performance of this product.

5 or 10 kg composites. Storage life 2 years minimum in unopened tins, stored at 5°C-40°C. Colour Grey. Specific gravity 1.14 – 1.25 gcm-3 (mixed)